| Composition | Corrosion protection1) | Coeff. of | Finish | ||
|---|---|---|---|---|---|
| Zn-Corr. | Fe-Corr. | friction | |||
| SurTec 520 | O; PE | 20-30 h | 50-150 h | 0.09-0.13 | technically bright |
| SurTec 521 | O; PE | 20-30 h | 50-150 h | 0.10-0.14 | matte |
| SurTec 522 | M; PE-Si | 40-60 h | 150-250 h | 0.09-0.13 | technically bright |
| SurTec 555 | O; PE-PA | 30-40 h | 100-150 h | - | bright |
| SurTec 555 S | M; PE-PA-Si | 50-100 h | 150-350 h | - | bright |
| SurTec 556 | I; Si | 50-80 h | 150-350 h | - | technically bright |
| SurTec 556 GL | M; PE-Si | 50-100 h | 150-350 h | 0.09-0.13 | technically bright |
| SurTec 556 RT | M; PE-Si | 50-100 h | 150-350 h | 0.11-0.15 | bright |
| SurTec 558 Black | O; PA-PS | 50-100 h | 150-350 h | - | bright |
| 1) = DIN 50021 SS; additional delay | P = polymer dispersion | |
| PE = polyethylene | ||
| O = organic sealing | PA = polyacrylate | |
| I = inorganic sealing | PS = polystyrene | |
| M = inorganic and organic components | Si = silicium compounds |